THIXO AGENT FOR ADDITION SILICONES – agent for thixotroping of additive silicone
THIXO AGENT CONDENSATION SILICONE – agent for thixotroping of polycondensation silicone
DYES: black, brownish, red, green, yellow, blue, white and orange
RTV2 Silicone
RTV2 Silicone is a versatile, high-performance two-component room temperature vulcanizing (RTV) silicone rubber designed for a wide range of applications. This premium silicone material is renowned for its excellent flexibility, durability, and ease of use, making it ideal for both industrial and artistic purposes.
Key Features:
- Two-Component System: RTV2 Silicone comes as a two-part system consisting of a base and a curing agent, which, when mixed, cures at room temperature to form a flexible, durable silicone rubber.
- Excellent Mold-Making Properties: With its superior flowability and low viscosity, RTV2 Silicone captures fine details accurately, making it perfect for mold-making in the arts, crafts, and manufacturing sectors.
- High Tear and Tensile Strength: The cured silicone exhibits excellent mechanical properties, including high tear resistance and tensile strength, ensuring longevity and durability in the final product.
- Temperature Resistance: RTV2 Silicone can withstand a wide range of temperatures, maintaining its properties from -60°C to 200°C, making it suitable for various environments and applications.
- Chemical Resistance: It is resistant to a variety of chemicals, including acids, bases, and solvents, ensuring reliability and stability in demanding conditions.
- Easy to Use: The mixing ratio of the base to the curing agent is straightforward, and the silicone <>cures quickly at room temperature, simplifying the mold-making and casting processes.
Applications:
- Mold Making: Ideal for creating detailed molds for casting resins, plasters, waxes, and low-melt metals.
- Prototyping: Used in the creation of prototypes and models in product development.
- Art and Sculpture: Popular among artists and sculptors for its ability to reproduce fine details.
- Industrial Manufacturing: Utilized in the production of gaskets, seals, and various other industrial components.
- Food-Grade Molds: Certain formulations of RTV2 Silicone are suitable for food-grade applications, including chocolate and candy molds.
How to Use:
- Preparation: Ensure that the surfaces to be molded are clean and free of contaminants. Apply a mold release agent if necessary.
- Mixing: Measure the base and curing agent according to the recommended ratio (typically 1:1 or 10:1 by weight). Mix thoroughly to ensure a uniform blend.
- Pouring: Pour the mixture into the mold frame, ensuring that it covers all areas evenly. Use a vacuum chamber to remove air bubbles if required.
- Curing: Allow the silicone to cure at room temperature for the specified time (typically 24 hours). For faster curing, slight heating may be applied.
- Demolding: Carefully remove the cured silicone mold from the frame. It is now ready for use.
RTV2 Silicone is the perfect choice for professionals and hobbyists alike who demand high-quality, reliable, and versatile silicone rubber for their projects. Whether you're casting detailed sculptures or producing industrial components, RTV2 Silicone delivers exceptional performance and results.
Polyaddition (platinum catalyst)
←
→
| Product name | Mixing ratio (pbw) | Color | Viscosity (mPa.s) | Pot life (23°C - min) | Demoulding time (23°C) | Hardness (Shore A) | Elongation at break (%) | Tear strength (kN/m) |
|---|---|---|---|---|---|---|---|---|
ZA OF1 | 100:100 | semi-transparent | 1000 | 12 | 60 min | gel | - | - |
ZA 35-15 GLASS | 100:100 | transparent | 200 | 45 | 6 hours | 20 | - | - |
ZA 00 Translucent | 100:100 | semi-transparent | 1500 | 17 | 1 hour 30 minutes | 0 | 5.5 | 4 |
ZA 4 LT | 100:100 | 1700 | 12 | 1 hour 30 minutes | 4 | 500 | 4.5 | |
ZA 8 LT | 100:100 | semi-transparent | 1000 | 17 | 2 hours | 8 | 280 | 3 |
ZA 12 LT BLU | 100:100 | 3500 | 16 | 2 hours | 12 | 550 | 9 | |
ZA 10 Orange | 100:100 | 4500 | 15 | 2 hours | 13 | 600 | 17 | |
ZA 13 WT45 | 100:100 | semi-transparent | 4500 | 45 | 3 hours | 13 | 450 | 14 |
ZA 16 Fast | 100:100 | 3500 | 10 | 1 hour | 16 | 400 | 9 | |
ZA 22 Mould | 100:100 | 4000 | 17 | 1 hour | 22 | 380 | 20 | |
ZA 22-45 Mould Neutro | 100:100 | 4000 | 45 | 7 hour | 22 | 380 | 20 | |
ZA 30 Antistatic | 100:100 | 17000 | 10 | 2 hours | 30 | 370 | 26 | |
ZA TT 1240 | 100:100 | 5500 | 40 | 3 hours | 12 | 600 | 17 | |
ZA TT 2240 | 100:100 | 7500 | 40 | 3 hours | 22 | 500 | 16 | |
ZA TT 3040 | 100:100 | 10000 | 40 | 4 hours | 30 | 460 | 21 | |
ZA RTV 20-45 | 100:100 | 4500 | 50 | 4 hours | 20 | 600 | 15 | |
ZA RTV 30-45 | 100:100 | 5000 | 50 | 4 hours | 30 | 450 | 15 | |
ZA RTV 30-60 | 100:100 | 6000 | 80 | 8 hours | 30 | 500 | 18 | |
ZA RTV 40-45 | 100:100 | 5500 | 50 | 4 hours | 40 | 250 | 15 | |
ZA 43 PU | 100:100 | 12000 | 20 | 3 hours | 43 | 400 | 12 | |
ZA 50 LT | 100:100 | 20000 | 17 | 3 hours | 50 | 320 | 12 | |
ZA 28 Mould | 100:100 | 4000 | 16 | 1 hour | 28 | 500 | 8 | |
ZA 35 Mould | 100:100 | 4000 | 12 | 1 hour | 35 | 310 | 8 | |
ZA 35 Mould Fast | 100:100 | 4000 | 7 | 40 min | 35 | 300 | 8 | |
ZA 50 Mould Orange | 100:100 | 5000 | 15 | 3 hours | 50 | 150 | 5 | |
ZA 22 Thixo Body | 100:100 | 50000 | 6 | 15 min | 22 | 400 | 14 | |
ZA SFX 10 WT10 | 100:100 | semi-transparent | 10000 | 12 | 40 | 10 | 650 | 14 |
MarkPlus | 100:100 | plasticine | 12 | 3 hours | 37 | 176 | 5 | |
ZA 25-6 Spray Self Bond | 100:100 | semi-transparent | 8000 | 6 | 30 mins | 25 | 420 | 26 |
ZA 26 WT10 Spray Self Bond | 100:100 | semi-transparent | Thixo | 10 | 60 min | 25 | 400 | 20 |
HT 24 WT5 | 100:100 | semi-transparent | 7000 | 5 | 30 mins | 24 | 430 | 14 |
HT 24 Transparent | 100:100 | semi-transparent | 7000 | 22 | 3 hours | 24 | 430 | 14 |
HT 33 Transparent | 100:100 | semi-transparent | 7500 | 22 | 3 hours | 33 | 430 | 16 |
HT 33 Rosso | 100:100 | 7500 | 20 | 4 hours | 33 | 460 | 20 | |
HT 42 Grey | 100:100 | 24000 | 24 | 2 hours | 42 | 350 | 17 | |
HT 45 Transparent | 100:100 | semi-transparent | 8500 | 11 | 1 hour 30 minutes | 43 | 370 | 19 |
XTX 45 Oil Bleeding | 100:10 | transparent | 50000 | 75 | 15 hours | 41 | 350 | 21 |
XTX 45 Dry | 100:10 | transparent | 35000 | 90 | 15 hours | 43 | 400 | 21 |
ZAX 60 | 100:10 | 100000 | 60 | 24 hours | 60 | 200 | 10 |
High dimensional accuracy and stability, high mechanical parameters, low shrinkage factor
Polycondensation
←
→
| Designation | Mixing ratio (by weight) | Color | Viscosity (mPa.s) | Pot life (min-23°C) | Demoulding Time (23°C) | Hardness (Shore A) | Elongation at break (%) | Tear strength (kN/m) |
|---|---|---|---|---|---|---|---|---|
ZC 10 | 100 : 5 | white | 25.000 | 90 | 24 hours | 14 | 500 | 16 |
ZC 20 | 100 : 5 | white | 25.000 | 90 | 24 hours | 21 | 350 | 17 |
ZC 30 | 100 : 5 | white | 27.000 | 90 | 24 hours | 30 | 250 | 15 |
ZC PUTTY 2528 | 100 : 4 | Off-white | Putty | 90 | 20 hours | 30 | 200 | 3.6 |
Polycondensation silicone