RTV2 Силикон is a versatile, high-performance two-component room temperature vulcanizing (RTV) silicone rubber designed for a wide range of applications. This premium silicone material is renowned for its excellent flexibility, durability, and ease of use, making it ideal for both industrial and artistic purposes.



Key Features:
  • Two-Component System: RTV2 Silicone comes as a two-part system consisting of a base and a curing agent, which, when mixed, cures at room temperature to form a flexible, durable silicone rubber.
  • Excellent Mold-Making Properties: With its superior flowability and low viscosity, RTV2 Silicone captures fine details accurately, making it perfect for mold-making in the arts, crafts, and manufacturing sectors.
  • High Tear and Tensile Strength: The cured silicone exhibits excellent mechanical properties, including high tear resistance and tensile strength, ensuring longevity and durability in the final product.
  • Temperature Resistance: RTV2 Silicone can withstand a wide range of temperatures, maintaining its properties from -60°C to 200°C, making it suitable for various environments and applications.
  • Chemical Resistance: It is resistant to a variety of chemicals, including acids, bases, and solvents, ensuring reliability and stability in demanding conditions.
  • Easy to Use: The mixing ratio of the base to the curing agent is straightforward, and the silicone <>cures quickly at room temperature, simplifying the mold-making and casting processes.


Applications:
  • Mold Making: Ideal for creating detailed molds for casting resins, plasters, waxes, and low-melt metals.
  • Prototyping: Used in the creation of prototypes and models in product development.
  • Art and Sculpture: Popular among artists and sculptors for its ability to reproduce fine details.
  • Industrial Manufacturing: Utilized in the production of gaskets, seals, and various other industrial components.
  • Food-Grade Molds: Certain formulations of RTV2 Silicone are suitable for food-grade applications, including chocolate and candy molds.


How to Use:
  1. Preparation: Ensure that the surfaces to be molded are clean and free of contaminants. Apply a mold release agent if necessary.
  2. Mixing: Measure the base and curing agent according to the recommended ratio (typically 1:1 or 10:1 by weight). Mix thoroughly to ensure a uniform blend.
  3. Pouring: Pour the mixture into the mold frame, ensuring that it covers all areas evenly. Use a vacuum chamber to remove air bubbles if required.
  4. Curing: Allow the silicone to cure at room temperature for the specified time (typically 24 hours). For faster curing, slight heating may be applied.
  5. Demolding: Carefully remove the cured silicone mold from the frame. It is now ready for use.


RTV2 Silicone is the perfect choice for professionals and hobbyists alike who demand high-quality, reliable, and versatile silicone rubber for their projects. Whether you're casting detailed sculptures or producing industrial components, RTV2 Silicone delivers exceptional performance and results.

Polyaddition (platinum catalyst)
Product nameMixing ratio
(pbw)
ColorViscosity
(mPa.s)
Pot life (23°C - min)Demoulding time
(23°C)
Hardness
(Shore A)
Elongation at break
(%)
Tear strength
(kN/m)
ZA OF1
100:100semi-transparent10001260 mingel--
ZA 35-15 GLASS
100:100transparent200456 hours20--
ZA 00 Translucent
100:100semi-transparent1500171 hour 30 minutes05.54
ZA 4 LT
100:100
1700121 hour 30 minutes45004.5
ZA 8 LT
100:100semi-transparent1000172 hours82803
ZA 12 LT BLU
100:100
3500162 hours125509
ZA 10 Orange
100:100
4500152 hours1360017
ZA 13 WT45
100:100semi-transparent4500453 hours1345014
ZA 16 Fast
100:100
3500101 hour164009
ZA 22 Mould
100:100
4000171 hour2238020
ZA 22-45 Mould Neutro
100:1004000457 hour2238020
ZA 30 Antistatic
100:10017000102 hours3037026
ZA TT 1240
100:100
5500403 hours1260017
ZA TT 2240
100:100
7500403 hours2250016
ZA TT 3040
100:100
10000404 hours3046021
ZA RTV 20-45
100:100
4500504 hours2060015
ZA RTV 30-45
100:100
5000504 hours3045015
ZA RTV 30-60
100:1006000808 hours3050018
ZA RTV 40-45
100:100
5500504 hours4025015
ZA 43 PU
100:100
12000203 hours4340012
ZA 50 LT
100:100
20000173 hours5032012
ZA 28 Mould
100:100
4000161 hour285008
ZA 35 Mould
100:100
4000121 hour353108
ZA 35 Mould Fast
100:100
4000740 min353008
ZA 50 Mould Orange
100:100
5000153 hours501505
ZA 22 Thixo Body
100:100
50000615 min2240014
ZA SFX 10 WT10
100:100semi-transparent1000012401065014
MarkPlus
100:100
plasticine123 hours371765
ZA 25-6 Spray Self Bond
100:100
semi-transparent
8000630 mins2542026
ZA 26 WT10 Spray Self Bond
100:100
semi-transparent
Thixo1060 min2540020
HT 24 WT5
100:100semi-transparent7000530 mins2443014
HT 24 Transparent
100:100semi-transparent7000223 hours2443014
HT 33 Transparent
100:100semi-transparent7500223 hours3343016
HT 33 Rosso
100:100
7500204 hours3346020
HT 42 Grey
100:100
24000242 hours4235017
HT 45 Transparent
100:100semi-transparent8500111 hour 30 minutes4337019
XTX 45 Oil Bleeding
100:10transparent500007515 hours4135021
XTX 45 Dry
100:10transparent350009015 hours4340021
ZAX 60
100:10
1000006024 hours6020010

High dimensional accuracy and stability, high mechanical parameters, low shrinkage factor

Polycondensation
DesignationMixing ratio
(by weight)
ColorViscosity
(mPa.s)
Pot life
(min-23°C)
Demoulding Time
(23°C)
Hardness
(Shore A)
Elongation at break
(%)
Tear strength (kN/m)
ZC 10
100 : 5white25.0009024 hours1450016
ZC 20
100 : 5white25.0009024 hours2135017
ZC 30
100 : 5white27.0009024 hours3025015
ZC PUTTY 2528
100 : 4Off-whitePutty9020 hours302003.6

Polycondensation silicone

THIXO AGENT FOR ADDITION SILICONES – agent for thixotroping of additive silicone

THIXO AGENT CONDENSATION SILICONE – agent for thixotroping of polycondensation silicone

DYES: black, brownish, red, green, yellow, blue, white and orange

Other products: